简介：Theeffectofnonmetallicinclusionsinthedropletofthestainlesssteelcoveredelectrodeontheporositywasresearched.Theresultshowsthatthenonmetallicinclusionsinthedropletarespherical,theircompositionisdifferentfromtheoneofslagandtheinclusionshavethecharacterof"innerformation".Whentheratioofrutiletoilmeniteinthecoatedmaterialisincreased,thedropletbecomescoarse,thecontentofnonmetallicinclusioninthedropletdecreases,andtheporositysensitivityintheweldmetalalsodecreases.Whentheratiooffledspartoilmeniteinthecoatedmaterialisincreased,thedropletbecomesfine,thecontentofnonmetallicinclusioninthedropletincreases,andtheporositysensitivityintheweldmetalincreases.WhentheratioofFe2O3toilmeniteinthecoatedmaterialisincreased,thedropletbecomesfine,thecontentofnonmetallicinclusiondecreases,whiletheporositysensitivitydoesnotreduce.

简介：WeldingresearchofA6N01S-T5aluminumalloyprofileforhigh-speedtrainwasdonebyusinglaser-MIGhybridweldingandMIGweldingindividually.Andtheweldappearance,weldingdistortion,mechanicalpropertiesofthejointsandmicrostructureswereanalyzed.Thetestresultsdemonstratedthathigh-efficientweldingfortheprofilecanbeachievedbyusinglaser-MIGhybridwelding,thespeedofwhichcanbeover3.0m/min.Theprocessinghadagoodgapbridgingability，evenifthegapofthebuttjointwasupto2.0mm,agoodweldappearancecanalsobegot.Whilethehybridweldingspeedwasgreaterthan2.5m/min,theweldingdistortionofthelaser-tandemMIGhybridjointswasjustabout33%ofthatoftheMIGjoints,buttheweldingefficiencywasover3timesofMIGwelding.Andtensilestrengthofthehybridjointswas85%ofthatofA6N01S-T5basemetal,9%higherthanthatoftheMIGjoints.Fatiguepropertieswastestedindividuallywithpulsedtensilefatiguemethodintheconditionof1×107lifetime.Thetestresultsdemonstratedthatthefatiguestrengthofthejointswasalittlelowerthanthatofbasematerial,whichcouldbeupto115MPa.Butthefatiguestrengthofhybridweldingjointswas107.5MPa,whichwas23%higherthan87MPaofMIGweldingjoints.

简介：ThesusceptibilityofweldedjointfortheX65pipelinesteeltoH2Sstresscorrosioncracking(SCC)isinvestigated.SCCtestsonthesteelarecarriedoutintheenvironmentbasedonNACETM-01-77solutionwithsaturatedgaseousH2S.Thethresholdstressintensityfactorandcrackpropagationvelocityarecalculatedaccordingtowedge-openingloading(WOL)specimens.Thethree-dimensionalelastic-plasticfiniteelementanalysisofWOLspecimensisperformedbyusingtheFEMprogrammingpackageANSYS.Stressfieldandconcentrationofhydrogendistributionpropertyaheadofthecracktipareobtained.ThispapersurveyedthemicrostructureofweldedjointandstudiedonthemechanicalpropertiesofX65pipelinesteel.Itprovidesexperimentalbasisforstudyingstresscorrosion.Theresultsofnumericalanalysisareconsistentwithconclusionsofstresscorrosiontest.

简介：随着核电、高铁、海洋工程等行业的发展,现有焊接人才已满足不了经济发展和技术创新的需求,有的已影响到新产品的开发和质量控制,尤其是应用型焊接人才已成为阻碍产业升级的重要因素。笔者结合多年来参加焊接工程项目的体会,从应用型焊接人才培养的紧迫性入手,分析了目前应用型焊接人才培养中存在的问题,探索性的提出了解决问题的策略,并就如何实现高质量、快节奏培养应用型焊接人才方法进行了探讨。

简介：<正>最近,成都焊研科技有限责任公司"基于总线控制技术的整体式后桥总成自动焊装生产线"相关核心技术已申请了4项国家发明专利和1项实用新型技术专利,并获得科技型中小企业技术创新基金立项证书。