简介:Forenhancingthe2.0μmbandfluorescenceofHo3+,acertainamountofWO3oxidewasintroducedintoHo3+/Tm3+/Yb3+tri-dopedtelluriteglasspreparedusingmelt-quenchingtechnique.Thepreparedtri-dopedtelluriteglasswascharacterizedbytheabsorptionspectra,fluorescenceemissionandRamanscatteringspectra,togetherwiththestimulatedabsorption,emissioncross-sectionsandgaincoefficient.TheresearchresultsshowthattheintroductionofWO3oxidecanfurtherimprovethe2.0μmbandfluorescenceemissionthroughtheenhancedphonon-assistedenergytransfersbetweenHo3+/Tm3+/Yb3+ionsundertheexcitationof980nmlaserdiode(LD).Meanwhile,themaximumgaincoefficientofHo3+at2.0μmbandreachesabout2.36cm-1.Anintense2.0μmfluorescenceemissioncanberealized.
简介:Wepresenttherecentresearchprogressesofourgrouponmid-infraredpulsedfiberlasersat3μmbypassiveswitching.Threedifferentkindsofsaturableabsorbersincludingsemiconductorsaturableabsorber(SESAM),Fe2+:ZnSecrystal,andtopologicalinsulator(TI)wereusedtoperformthepulsegeneration,respectively.Thetemporalregimesofmodelocking,Q-switching,andQ-switchinginducedgainswitchingweregained.Somerelativediscussionsandprospectiveeffortsareproposedattheendofthispaper.
简介:Er3+/Ce3+共掺碲酸盐玻璃的组成teo2-geo2-li2o-nb2o5使用常规的熔融淬火技术在Er3+的潜在应用掺铒光纤放大器(EDFA)的制备。测定了玻璃样品的吸收光谱、上转换光谱和1.53μm波段荧光光谱。结果表明,1.53μm波段的荧光发射强度的Er3+掺杂的碲酸盐玻璃光纤与Ce3+引入适量明显改善,这是由于能量转移(ET)Er3+Ce3+。同时,1.53μm波段的光信号放大是基于速率方程和功率传输方程模拟,并在约2.4dB信号增益的增量在1532nmEr3+/Ce3+共掺碲酸盐玻璃纤维被发现。最大信号增益达到29.3dB的一个50厘米长的光纤在980nm泵浦功率为100MW,结果表明所制备的Er3+/Ce3+共掺碲酸盐玻璃是一个很好的增益介质的应用1.53μM宽带高增益掺铒光纤放大器。
简介:一个透明的3-巯基丙基三甲氧基硅烷(MPTMS)/银/氧化钼复合阳极制备绿色有机发光二极管(OLED)。研究了亮度复合阳极和有机电致发光器件的工作电压的影响。通过优化各层的MPTMS/银/氧化钼结构的厚度,对MPTMS/银的透光率(8nm)/MoO3(30nm)达到75%以上在520nm左右。的薄层电阻为3.78?/□,与此相应的MPTMS/Ag(8nm)/MoO3(30nm)的结构。为优化阳极的有机电致发光器件的电致发光(EL),最大电流效率达到4.5cd/A,最大亮度是37和036cd/m2。此外,通过优化阳极的有机电致发光器件具有非常低的工作电压(2.6V)获得100cd/m2的亮度。我们认为,改进的设备性能主要是由于增强的空穴注入造成的减少孔注入势垒高度。我们的研究结果表明,使用MPTMS-SAMs/银/氧化钼作为复合阳极可以在低工作电压和高亮度OLED的制作一个简单的和有前途的技术。
简介:Superluminescencediode(SLD)moduleswithwidespectrumcharacteristicsarerequiredinfibergyroscopes.A1.3μmbutterflypackagedsuperluminescencediodewiththespectrumwidthover30nmisreportedandrecentadvancesinprocessofSLDisdescribedinthepaper.TheSLDmoduleshavebeenappliedtofibergyroscopes.
简介:Asimpleandeffectivegreedyalgorithmforimageapproximationisproposed.Basedonthematchingpursuitapproach,itischaracterizedbyareducedcomputationalcomplexitybenefitingfromtwomajormodifications.First,ititerativelyfindsanapproximationbyselectingMatomsinsteadofoneatatime.Second,theinnerproductcomputationsareconfinedwithinonlyafractionofdictionaryatomsateachiteration.Themodificationsareimplementedveryefficientlyduetothespatialincoherenceofthedictionary.Experimentalresultsshowthatcomparedwithfullsearchmatchingpursuit,theproposedalgorithmachievesaspeed-upgainof14.4~36.7timeswhilemaintainingtheapproximationquality.