简介：Coprecipitationsupercriticalfluiddryingtechnologyhasbeenemployedtosynthesizecalcia-stabilizedzirconiaultrafinepowderwithlow-costinorganicsaltsasthestartingmaterials.Thesinteringbehaviorsofthesepowderswerealsoinvestigated.Theresultsshowedthatsupercriticalfluiddryingcouldeffectivelyalleviatethehardagglomerationofgrainsduringthegeldryingprocess,andthemorphologyofthepowderretainedthenetworktextureoftheoriginalgel.Theresultingparticleswerecharacterizedbysmallparticlesize(5～20nm),bettermonodispersityandhighsurfacearea,whichgaverisetohighactivityandsinterability.Consequently,thesepowderscouldreadilybecompactedintothedesiredshapeandtheirdensificationcouldbecarriedoutinshortertimeandatlowertemperatures.Forinstance,nanometer-sizedpowdercalcinedat600℃for2hcouldbecold-pressedintoagreenbodyandsinteredat1100°for0.5htoattainadensebodywithbulkdensityof5.9718g/cm3andspecificporevolumeof0.0008cm3/g.

简介：

简介：SiO2-B2O3-Al2O3-CaO在低sintering温度使契约成玻璃，高力量被讨论。FTIR和XRD分析被用来与铝的不同内容描绘基本使成玻璃的契约的结构。弯曲力量和热扩大系数也被测试。同时，在660光线衍射(XRD)的sintering温度的合成标本的微观结构，扫描电子显微镜(SEM)分析和其它工具。结果证明分别地，钾和磷的溶解率在95.64wt%lessthan的一种谷物尺寸的条件下面是70wt%和93.7wt%0.074公里，9.78gg-1硫磺的酸，0.5gg-1铵氟化物，160桴???瑳畲瑣牵獥椠?慭湩慴湩摥映吗？？

简介：这学习介绍鸡蛋壳的使用利用手掌的废物基于的核壳通过他们的表面的修正激活碳(PKSAC)到提高H的吸附能力2S。反应表面方法论技术被用来优化过程条件，他们被发现是：为H2S起始的集中，在接触时间的540min和为吸附物的1g集中。三安排的影响H2S移动效率和使妊娠的交流产量被调查。两回答IAC收益(IACY，%)并且移动效率(RE，%)被最大化优化IAC准备条件。为IACY和RE的最佳准备条件如下被发现：880的IAC的锻烧温度???ì

简介：利用DTA、XRD研究了Y2O3的添加对CaO-MgO-SiO2系陶瓷纤维析晶行为的影响。根据Ozawa和Kissinger法对系统中析晶活化能的计算结果表明，少量Y2O3的添加并没有改变材料中析出的晶相种类，但是可以提高玻璃化转变温度和析晶温度，增大晶相的析晶活化能，从而能够在一定程度上抑制材料中晶相的析出。

简介：铁磁性微晶玻璃由于具有磁性和生物活性，可以用作磁感应热疗的热种子材料。采用SiO2-Na2O-CaO-P2O5-Fe2O3五元系统，通过共沉淀-熔融法和熔融法两种不同的方法制备铁磁性微晶玻璃，利用XRD确定其晶相并计算晶体的晶格常数和晶粒尺寸，并通过VSM表征样品的磁性能。结果表明，玻璃液在自然冷却的过程中就形成了大量的磁铁矿，不经过热处理过程即可制得具有磁铁矿唯一晶相的铁磁性微晶玻璃并具有生物活性。共沉淀-熔融法制备的样品磁性更强。