简介:ThehigherorderasymptoticfieldsatthetipofasharpV-notchinapower-hardeningmaterialforplanestrainproblemofModeⅠarederived.Theorderhierarchyinpowersofrforvarioushardeningexponentsnandnotchanglesβisobtained.Theangulardistributionsofstressforseveralcasesareplotted.Theself-similaritybehaviorbetweenthehigherordertermsisnoticed.ItisfoundthatthetermswithhigherordercanbenegleetedfortheV-notchangleβ>45°.
简介:Basedonthethermodynamictheory,anorthotropicdamageconstitutivemodelwasdevelopedtodescribethenonlinearmechanicalbehaviorofC/SiCcomposites.Thediferentnonlinearkinematicandisotropichardeningfunctionswereadoptedtodescribeaccuratelythedamageevolutionprocesses.Thedamagevariablesweredefinedwiththedamagedmodulusandtheinitialundamagedmodulusonenergyequivalenceprinciple.Theinitialorthotropyanddamagecouplingwerepresentedinthedamageyieldfunction.Tensileandin-planeshearloadingandunloadingtestswereperformed,andagoodagreementbetweenthemodelandtheexperimentalresultswasachieved.