简介：1Cr18Ni9Ti不锈钢球头在焊接后经酸洗，表面存在粗糙的腐蚀凹坑。通过采用S-3700N扫描电子显微镜、能谱分析仪、金相显微镜等对表面粗糙的腐蚀凹坑进行成因分析。结果表明：球头在焊接过程中产生了局部敏化现象，球头的晶粒组织细于与之配合的外套螺母组织，使得球头的耐腐蚀性低于外套螺母，在酸洗去氧化皮的过程中，外套螺母与球头的焊缝区、接管嘴的焊缝区之间形成缝隙，酸洗液中的正负离子移动受到了阻滞，导致缝隙处发生严重腐蚀，最终表现为球头表面的点状腐蚀形貌。定期更换酸洗槽液，降低Cl-浓度，以及在酸洗过程中活动零件，可以减少该类腐蚀的产生。

简介：Anewenvironmentalfriendlycatalyst,H4SiW12O40/PAnwaspreparedandidentifiedbymeansofFT-IR,XRDandTG/DTA.Cyclohexanone1,2-propanediolketalwassynthesizedfromcyclohexanoneand1,2-propanediolinthepresenceofH4SiW12O40/PAn.Thefactorsinfluencingthesynthesiswerediscussedandthebestconditionswerefoundout.Theoptimumconditionsare:molarratioofcyclohexanoneto1,2-propanediolis1:1.4,thequantityofcatalystisequalto1.0%offeedstocks,andthereactiontimeis40min.H4SiW12O40/PAnisanexcellentcatalystforsynthesizingcyclohexanone1,2-propanediolketalanditsyieldcanreachover96.5%.

简介：CuNi10Fe1Mnalloybilletunderrotatingelectromagneticfield(REF)wascharacterizedinthiswork.ThechangeofthecrystalorientationwasfirstexploredbyX-raydiffraction(XRD)andscanningelectionmicroscope(SEM);thecorrosionresistancewasdonebythreeelectrodessystem,andthenaturalseawaterwasusedascorrosionmedium.Theresultsdemonstratethatthestrongestcrystalorientationistransformedfromcrystalplane(200)to(111);moreover,thecrystalplane(111)whoseintensityisthe...

简介：2009年TPCA先进技术研讨会暨标竿论坛于8月6日正式登场，第一场演讲由Prismark姜旭高博士揭开序幕，主题为PCB技术发展趋势与市场商机分析。姜旭高说，比起半导体产业来说，PCB技术发展速度相当缓慢，2000年以来，全球PCB产值几乎没有什么变化，但是台湾PCB厂的产值却大增一倍，在经过这次金融风暴之后，台湾PCB厂展现惊人的生存力，预料未来1-2年内，台湾PCB产业将可跃居全球领先地位。

简介：虽然中铝、五矿对澳洲矿企的投一度遭遇波折，但这不能阻挡中资企业海外收购的步伐。澳洲中小型矿商MetallicaMinerals16日发布公告，称中国吉恩镍业（上海交易所代码：600432）的母公司吉林吴融有色金属集团，已通过场外交易的方式收购了该公司1400万股股票，正式成为公司的第一大股东。

简介：1．价格走势分析1．1国际铂价受日本地震影响大幅下跌2010年，由于需求改善，铂价震荡上行，年末上涨至1750美元／盎司。2011年初，铂价承接去年的上涨趋势，1月中旬在投资者推动下上涨至1800美元／盎司，随后铂价出现小幅回调。2月初，受南非供应吃紧影响铂再次发力，快速突破1850美元阻力，2月9日最高达到1864．5美元／盎司。

简介：针对激光直接沉积修复的1Cr15Ni4Mo3N钢零件在磁粉检测时出现的磁痕现象,采用接触通电、湿磁粉连续法,对设计的试样进行磁粉检测,确定磁痕显示位置;利用光学显微镜对磁痕显示处形貌及修复接头和组织进行观察和研究,分析磁痕的性质和形成原因。研究发现:激光直接沉积修复1Cr15Ni4Mo3N钢在磁粉检测过程中与修复区外轮廓完全重合的磁痕显示是伪磁痕显示,主要是由修复区与基体中奥氏体含量的差异造成的。

简介：采用Gleeble热模拟方法研究Mg-6Zn-1Al-0.3Mn变形镁合金在温度为200-400°C，应变速率为0.01-7s-1条件下的热压缩变形行为。结果表明，变形温度和应变速率显著影响其热变形行为。通过计算获得了热变形激活能及应力指数分别为Q=166kJ/mol，n=5.99，且其本构方程为ε＆=3.16×1013[sinh（0.010σ）]5.99exp[-1.66×105/（RT）]。热压缩显微组织观察表明：在应变速率为0.01-1s-1的条件下，在250°C热压缩变形时初始晶粒晶界及孪晶处发生了部分动态再结晶，而在高温（350-400°C）条件下，发生了完全动态再结晶且再结晶晶粒尺寸随着应变速率的增加而减小。获得的较优的变形条件为温度330-400°C、应变速率为0.01-0.03s-1以及350°C、应变速率为1s-1。

简介：2019年1-2月份,规模以上工业增加值同比实际增长5.3%(以下增加值增速均为扣除价格因素的实际增长率),增速较2018年12月份回落0.4个百分点。据测算,剔除春节因素影响增长6.1%。从环比看,2月份,规模以上工业增加值比上月增长0.43%。

简介：1—5月份，安徽省产金4．34吨，同比增长27．6％，完成年计划的48．2％：实现工业增加值、销售收入、利润同比分别增长42．9％、41．7％和40．0％。

简介：为了研究触变注射成形AZ91D合金中固相颗粒的形貌演变和液相的凝固行为,对该合金的组织和凝固行为进行了试验观察和理论分析。典型触变注射成形AZ91D合金由α-Mg和β-Mg17Al12两相构成,α-Mg相又可分为未熔固相和初生固相。未熔固相主要有形貌较为接近球状的固相、形貌不规则的固相、内部含有小液池的固相以及包裹液相的固相4种形貌。形貌不规则的固相被认为是球状固相和包裹液相的固相的中间发展形貌,内部含有小液池的固相可能是包裹液相的固相的初级形貌,包裹液相的固相则可能发生破裂形成不规则固相,最终发展成球状固相。球状固相被认为是最理想的也是最终的固相形貌。初生固相在液相合金中形核并长大,直至有不稳定长大行为发生为止,较为细小、圆整,主要受冷却速率的影响。Mg-Al合金二元相图的分析结果与试验观察到的组织相吻合。

简介：研究1Cr17Ni2不锈钢中不同δ铁素体相含量变化分别在FeCl3溶液和HNO3＋HF溶液中的耐腐蚀行为。通过腐蚀失重率计算及光学金相显微镜、扫描电子显微镜的观察发现：在FeCl3溶液中,δ铁素体的存在减弱了1Cr17Ni2不锈钢的耐腐蚀性能,δ铁素体是优选腐蚀相;而在HNO3＋HF溶液中,δ铁素体的存在增强1Cr17Ni2不锈钢的耐腐蚀性能,优选腐蚀相则变成了回火索氏体。通过表面腐蚀形貌表征可以实现反推其受到腐蚀介质环境的性质,为1Cr17Ni2不锈钢腐蚀失效与预防提供可行的方法和依据。

简介：TheeffectsoftheintroductionofCetoLa_(1-x)Ce_xFe_(11.5)Si_(1.5)alloyson1:13phaseformationmechanism,thefirst-ordermagneticphasetransitionstrengtheningcharacteristics,andmagnetocaloricpropertywerestudied,respectively.Theresultsshowthattheformationmechanismsof1:13andLaFeSiphasesinLa_(1-x)Ce_xFe_(11.5)Si_(1.5)alloysarethesameasthoseofCe_2Fe_(17)andCeFe_2phasesinCe–Febinarysystem,respectively.ThesubstitutionofCein1:13phasewhichislimitedcanmakethefirst-ordermagneticphasetransitioncharacteristicsstrengthen,whichcanmakethermalandmagnetichysteresisincrease,thetemperatureintervaloftemperatureinducedphasetransitiondecrease,andthecriticalmagneticfieldoffield-inducedmagneticphasetransition(HC)increase,respectively.Owingtothelatticeshrinkof1:13phasewiththeincreaseinCecontent,theCurietemperatures(TC)showalineardecrease.Themaximumchangeinmagneticentropygraduallyincreasesduetothedecreaseintemperatureintervaloftemperature-inducedphasetransition,buttherelativecoolingcapacitiesareallabout80Jákg-1atmagneticfieldof2T.

简介：

简介：Basedonclustervariationmethod(CVM)andnaturaliterationmethod(NIM),order-disorderphasetransitionintheintercalationcompoundsM1/2TiS2issimulatedbycomputer.Thefavorableconditions,underwhich3a0×a0superstructureisformed,aregiven,andtheresultsareingoodagreementwiththeexperimentsandtheoreticalcalculations.TherelationshipbetweencriticaltemperatureandM-ion-vacancyinteractionparameterislinear.

简介：

简介：激光冲击强化是一种新型表面处理技术,利用高功率激光束冲击金属零件表面,在零件表面形成较大的残余压应力,可有效改善零件的疲劳性能。以发动机1Cr11Ni2W2MoV叶片为研究对象,对其进行了激光冲击强化处理,研究强化处理对材料的微观组织和疲劳性能的影响。研究结果表明：相比未处理试样,激光冲击强化在1Cr11Ni2W2MoV叶片材料表层形成较大的残余压应力,表层晶粒更为细化,叶片的疲劳寿命提高1.7倍。

简介：进入2015年1季度，国际黄金价格先扬后抑维持震荡下行态势；1季度伦敦金银协会（LBMA）黄金现货均价（下午定盘价）为1219．22美元／盎司，环比下跌5．78％。2015年1季度国际黄金行情，主要受到美国经济形势和美国货币政策主导，随着美国经济持续复苏经济数据走强，美元强势反弹美元指数在3月中旬一度突破百点大关（创12年来新高），金价不断受到打压；而美联储3月关于加息是否推迟言论再次推动金价反复震荡；相对于美国经济复苏开始走上加息通道，欧洲央行1月22日宣布启动欧版量化宽松政策，各国央行相机抉择纷纷降息降准应对欧洲央行QE，这加剧了国际金价的下行：1月希腊债务危机、3月中东也门局势升级也一度推动国际黄金行情短暂反弹，但黄金价格整体走势颓势依旧。

简介：1Cr15Ni4Mo3N沉淀硬化不锈钢螺栓零件在制造工序磁粉检测时，发现螺栓表面有一条疑似裂纹状线性磁痕显示，后采用荧光渗透检测方法进行辅助检测，原磁痕显示处未见异常荧光显示。结合金相试验分析发现，螺栓原材料内呈带状分布的残余奥氏体，破坏了基体组织和材料磁性的连续性导致出现磁痕显示。研究为该材料在零件制造中磁粉检测的磁痕判定提供了依据。

简介：Themicrostructuresofas-castandas-solutionMg–12Gd–2Er–1Zn–0.6Zralloyswereinvestigatedbyopticalmicroscopy（OM）,scanningelectronmicroscopy（SEM）,transmissionelectronmicroscopy（TEM）,highresolutiontransmissionelectronmicroscopy（HRTEM）X-raydiffraction（XRD）andselected-areaelectrondiffraction（SAED）inthepresentinvestigation.TheresultsshowthattheprimaryeutecticphaseMg5（Gd,Er,Zn）andsomeflocculentfeaturesarefoundintheas-castalloy;theSAEDpatternindicatesthattheseflocculentfeaturesarethedenseareasofstackingfaults.The14H-LPSOstructureprecipitatesinthetemperaturerangeof673–793K,andthevolumefractionof14H-LPSOstructureincreaseswiththeextensionofheatingtime;however,thereisnoprecipitationof14H-LPSOstructurewhenthetemperaturereachesupto803K.Inaddition,theMg5（Gd,Er,Zn）phasedissolvesgraduallyalongwiththeprecipitationof14H-LPSOstructure.